Soft and thick DLC deposited on AISI 316L stainless steel with nitriding as pre-treatment tested in severe wear conditions

Keyphrases

• Nitrides 100%
• Wear Conditions 100%
• Severe Wear 100%
• AISI 316L Stainless Steel 100%
• Adhesion 66%
• DLC Coating 66%
• Soft Steel 66%
• Plasma Nitriding 33%
• High Mass Loading 33%
• Self-sustaining 33%
• Low Friction Coefficient 33%
• Nitrided Layer 33%
• Mass Loss 33%
• Austenitic Stainless Steel 33%
• Coated Samples 33%
• Duplex 33%
• Erosion Wear Behaviors 33%
• Load Capacity 33%
• Minimum Load 33%
• High Hardness 33%
• Wear Damage 33%
• Fretting Wear 33%
• Film Thickness 33%
• Severe Disease 33%
• Protective Film 33%
• Soft Coatings 33%
• Wear Properties 33%
• Slurry Erosion Test 33%
• Nitriding Process 33%
• Fretting Test 33%
• Hard Layer 33%

Engineering

• Nitriding 100%
• Pretreatment 100%
• Severe Wear 100%
• Fretting 100%
• Plasma Nitriding 50%
• Mass Loss 50%
• Austenitic Stainless Steel 50%
• Nitride Layer 50%
• Load Limits 50%
• Hard Layer 50%
• Wear Property 50%
• Nitriding Process 50%
• Erosion Wear 50%
• Coefficient of Friction 50%

Material Science

• Nitriding 100%
• Fretting 100%
• Surface Property 50%
• Wear Property 50%
• Soft Coating 50%
• Film Thickness 50%
• Protective Coating 50%
• Austenitic Stainless Steel 50%