Thermal diffusivity measurements of porous CFRP specimens with different number of plies using pulsed thermography in transmission and reflection mode

Publikation: Beitrag in Buch/Bericht/TagungsbandKonferenzbeitrag

Abstract

Porosity in carbon fibre reinforced polymers (CFRP) degrades the engineering performance, especially the interlaminar shear strength. In this work the porosity of CFRP was successfully determined by means of pulsed thermography. Additionally 3D-xray computed tomography measurements were carried out. The observation time and the resulting thermal diffusivity were determined for 116 CFRP test specimens with different porosity levels and different number of plies. The samples were fabricated by using 5 ply, 10 ply and 20 ply laminates and the specimen thicknesses varied from 1.02 mm to 5.2 mm. The comparison of CFRP specimens with different number of plies shows similar results in the dependency of thermal diffusivity on porosity. The results show a very good correlation between transmission and reflection measurement methods. The surprising correlation between the effective medium theory and the experimental results allows a quantitative evaluation of porosity with pulsed thermography comparable to the quality of ultrasonic testing.
OriginalspracheEnglisch
TitelProceedings of 12th Quantitative InfraRed Thermography Conference
Seitenumfang10
PublikationsstatusVeröffentlicht - 2014
Veranstaltung12th Quantitative InfraRed Thermography Conference - Bordeaux, Frankreich
Dauer: 7 Jul 201411 Jul 2014

Konferenz

Konferenz12th Quantitative InfraRed Thermography Conference
Land/GebietFrankreich
OrtBordeaux
Zeitraum07.07.201411.07.2014

Schlagwörter

  • Active Thermography
  • Porosity

Fingerprint

Untersuchen Sie die Forschungsthemen von „Thermal diffusivity measurements of porous CFRP specimens with different number of plies using pulsed thermography in transmission and reflection mode“. Zusammen bilden sie einen einzigartigen Fingerprint.

Zitieren