Strain-ageing of low-alloyed multiphase high-strength steels

Ludovic Samek, Jakub Dykas, Emmanuel De Moor, Adam Grajcar

Publikation: Beitrag in FachzeitschriftArtikelBegutachtung

2 Zitate (Scopus)

Abstract

The strain-aging of low alloyed, multiphase high-strength steels with strain-induced austenite to martensite transformation was studied. The influence of prestrain, aging time, and temperature dependence of the static strain aging was carried out. Ageing temperatures between 60 and 220 C and aging times from 20 to 10,000 min were investigated. The choice of steel composition allowed studying the influence of alloying elements, such as Si and Al, on the static strain aging behavior. Samples after aging were studied using light-optical microscopy, X-ray diffraction, and in-depth transmission electron microscopy (TEM). The Harper model was used to describe the precipitation mechanisms occurring during aging. The study of thin foils after aging using TEM showed the precipitation of low temperature transition carbides in the microstructure, which was observed between 60 and 5000 min. By using X-ray diffraction, it was revealed that aging at 170 C for a long time caused a slight decrease of the retained austenite volume fraction, but the C content remained constant.

OriginalspracheEnglisch
Aufsatznummer439
FachzeitschriftMetals
Jahrgang10
Ausgabenummer4
DOIs
PublikationsstatusVeröffentlicht - Apr 2020

Fingerprint

Untersuchen Sie die Forschungsthemen von „Strain-ageing of low-alloyed multiphase high-strength steels“. Zusammen bilden sie einen einzigartigen Fingerprint.

Zitieren