Improving the ply/interleaf interface in carbon fibre reinforced composites with variable stiffness

Keyphrases

• Carbon Fiber Composite 100%
• Interleaf 100%
• Variable Stiffness 100%
• Elevated Temperature 40%
• Maleic Anhydride 40%
• Flexural Test 40%
• Polystyrene Layer 40%
• Polystyrene 20%
• Adhesion 20%
• Room Temperature 20%
• Stiffness 20%
• Glass Transition Temperature 20%
• Interlaminar Shear Strength 20%
• Carbon-epoxy Composite 20%
• CFRP Layer 20%
• Morphing Structures 20%
• Low Shear Stress 20%
• Adhesion Strength 20%
• Deployable Structures 20%
• Styrene 20%
• Poly(styrene-co-maleic anhydride) 20%
• Controllable Stiffness 20%
• Flexural Stiffness 20%
• Premature Failure 20%
• Thick Adherend Shear Test 20%
• Stiffness Loss 20%
• Flexural Strength 20%

Engineering

• Fiber-Reinforced Composite 100%
• Elevated Temperature 100%
• Room Temperature 50%
• Interlaminar Shear Strength 50%
• Epoxy Composite 50%
• Potential Application 50%
• Glass Transition Temperature (Tg) 50%
• Flexural Stiffness 50%
• Deployable Structure 50%
• Premature Failure 50%
• Bending Strength 50%

Material Science

• Carbon Fiber 100%
• Polystyrene 100%
• Fiber-Reinforced Composite 100%
• Film 50%
• Shear Testing 25%
• Shear Strength 25%
• Glass Transition Temperature 25%
• Bond Strength (Materials) 25%
• Flexural Strength 25%