Endurance limit and threshold stress intensity of die cast magnesium and aluminium alloys at elevated temperatures

Keyphrases

• Elevated Temperature 100%
• Threshold Stress Intensity 100%
• Endurance Limit 100%
• Limit Stress 100%
• Die Casting Magnesium Alloy 100%
• Die Cast Aluminum Alloy 100%
• Cyclic Stress Ratio 75%
• Porosity 50%
• Aluminum Alloy 50%
• Ambient Air 50%
• AlSi9Cu3(Fe) 50%
• Crit 50%
• Stress Intensity 50%
• Fatigue Crack 50%
• AE42 50%
• Low Temperature 25%
• Ultrasonic 25%
• Fracture Surface 25%
• Magnesium Alloy 25%
• AZ91D Magnesium Alloy 25%
• High Pressure Die Casting 25%
• Fatigue Test 25%
• Air Environment 25%
• (R)-1 25%
• AZ91 25%
• Load Ratio 25%
• Fracture Mechanics 25%
• S-N Curve 25%
• Critical Stress 25%
• Cyclic Frequency 25%
• Cyclic Load 25%
• Initial Crack 25%
• Warm Air 25%
• Casting Porosity 25%
• High-cycle Fatigue Property 25%
• Fatigue Failure 25%
• Non-propagating Fatigue Crack 25%
• Frequency Ratio 25%

Engineering

• Elevated Temperature 100%
• Threshold Stress 100%
• Stress Intensity 100%
• Endurance Limit 100%
• Cast Magnesium 100%
• Cyclic Stress 75%
• Fatigue Crack 75%
• Porosity 75%
• Ambient Air 50%
• Low-Temperature 25%
• Ultrasonics 25%
• Fracture Surface 25%
• Mechanical Fatigue Test 25%
• Fatigue Property 25%
• S-N Curve 25%
• Load Ratio 25%
• High Cycle Fatigue 25%
• Fracture Mechanic Test 25%
• Pressure Die 25%
• Frequency Ratio 25%
• Critical Stress 25%
• Fatigue Failure 25%
• Initial Crack 25%
• Az91 Alloy 25%

Material Science

• Magnesium Alloy 100%
• Stress Intensity 100%
• Aluminum Alloy 100%
• Fatigue Crack 75%
• Fracture Mechanics 25%
• High-Cycle Fatigue 25%