Einfluss von gussfehlern auf die dauerfestigkeit von aluminium- und magnesiumgusslegierungen

Keyphrases

• Aluminum Cast Alloy 100%
• Magnesium Cast Alloy 100%
• Endurance Limit 100%
• Casting Defects 100%
• Porosity 66%
• Stress Amplitude 66%
• Magnesium Alloy 66%
• Failure Probability 66%
• AlSi9Cu3(Fe) 66%
• Final Failure 33%
• Aluminum Alloy 33%
• High Pressure Die Casting 33%
• Defect Size 33%
• Fatigue Test 33%
• Fatigue Properties 33%
• Fatigue Limit 33%
• Number of Cycles 33%
• AM60 33%
• AZ91 33%
• Ultrasonic Equipment 33%
• Critical Stress 33%
• Stress Intensity 33%
• Fatigue Crack 33%
• AE42 33%
• Initial Crack 33%
• Intensity Value 33%
• Large Castings 33%

Engineering

• Cast Alloy 100%
• Endurance Limit 100%
• Casting Defect 100%
• Stress Amplitude 66%
• Failure Probability 66%
• Porosity 66%
• Final Failure 33%
• Ultrasonics 33%
• Defect Size 33%
• High Pressure Die Casting 33%
• Mechanical Fatigue Test 33%
• Fatigue Limit 33%
• Fatigue Property 33%
• Stress Intensity 33%
• Critical Stress 33%
• Initial Crack 33%
• Fatigue Crack 33%
• Az91 Alloy 33%
• Intensity Value 33%

Material Science

• Magnesium 100%
• Cast Alloy 100%
• Magnesium Alloy 100%
• Die Casting 50%
• Stress Intensity 50%
• Fatigue Crack 50%
• Aluminum Alloy 50%